| Colour |
Black / Red
(Other colour as agreed between supplier and purchaser) |
| Finish |
One Side Plain / Other Side Patterned |
| Tensile Strength |
For Temp. -10 ℃ to 55 ℃ -15 N / mm2 (Min.) |
| Elongation At Break |
For Temp. -10 ℃ to 55 ℃ -250% (Min.) |
| Insulation Resistance with Water |
10,00,000 MΩ (Min.) |
| Leakage Currrent |
10 μA (Max.) |
| Flame Retardence |
The Mat is retarded to fire. |
| Low Temperature Resistance |
No tear, break of crack is observed in Mats under force of 100N for 30 hrs. At -40±3 ℃ |
| |
|
| Aging Test ( Test Temp. -10 to 55℃) |
1. Tensile Strength
2. Elongation at Break |
Not less then 75% without Aging.
Not less then 75% without Aging. |
| Effect of NAOH, Transformer Oil, HCL ( For Temp. -10 to 55℃) |
1. Tensile Strength
2. Elonggation at Break |
Not less then 80% without Aging.
Not less then 80% without Aging. |
| |
|